| Green Modification of Cellulose Nanocrystals and Their Reinforcement in Nanocomposites of Polylactic Acid |
| Click here to download the full text |
| Citation of this paper: |
| Hits: 1430 |
| Download times: 1263 |
| Author Name | Affiliation | | Xue Jiang1,2,3,* | 1. Jiangsu Engineering and Technology Research Center for Functional Textiles, Jiangnan University, Wuxi, Jiangsu Province, 214122, China
2. Key Laboratory of Eco-textiles of Ministry of Education, School of Textile and Clothing, Jiangnan University, Wuxi, Jiangsu Province, 214122, China
3. State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangzhou, Guangdong Province, 510640, China | | Martin A. Hubbe4 | 4. Department of Forest Biomaterials, College of Natural Resources, North Carolina State University, Raleigh, NC 27695-8005, USA |
|
| Fund Project:The authors are grateful to the National Natural Science Foundation of China (grant Nos. 31570578 and 31270632), the Fundamental Research Funds for the Central Universities (grant No. JUSRP51622A) and the State Key Laboratory of Pulp and Paper Engineering (grant No. 201809). |
| |
| Abstract:Cellulose nanocrystals (CNCs) of rod-like shape were prepared from degreased cotton using sulfuric acid hydrolysis. The obtained CNC suspension was neutralized using a sodium hydroxide solution to remove the residual sulfuric acid and improve the thermal stability of the CNC particles. Then, poly(ethylene oxide) (PEO) was employed to modify the nanocrystals through entanglement and physical adsorption. The goal was to further improve the thermal stability and weaken the hydrophilicity of CNCs. Original and modified CNCs were dosed into a polylactic acid (PLA) matrix to prepare nanocomposites using a hot compression process. Results of the thermogravimetric analysis showed that the initial thermal decomposition temperature of the modified CNCs showed a 120℃ improvement compared to the original CNCs. That is, the thermal stability of the modified CNCs improved because of their shielding and wrapping by a PEO layer on their surface. Results from scanning electron microscopy and ultraviolet-visible spectrophotometry showed that the compatibility of the modified CNCs with organic PLA improved, which was attributed to the compatibility of the PEO chains adsorbed on the surface of the CNCs. Finally, the results of tensile tests indicated a significant improvement in terms of breaking strength and elongation at the break point. |
| keywords:cellulose nanocrystals thermal stability hydrophilicity polylactic acid compatibility nanocomposites |